15kg 1.2mm Welding Alloys LP-G Flux Core Mig Wire
$579.00
Product Introduction
15kg spool of 1.2mm Welding Alloys LP-G flux core mig wire, ideal for all-positional hardfacing in metal-metal wear and high abrasion applications like agricultural/earthmoving equipment. Martensitic steel deposit offers 55-60 HRC hardness, good impact resistance and machinability with special tools.
Product Parameters
| Wire Diameter | 1.2mm |
| Spool Weight | 15kg |
| Hardness | 55-60 HRC |
| Shielding Gas | Argon 5/2 or similar mixed gas |
| Polarity | DC+ |
15kg – 1.2mm Welding Alloys LP-G Hardfacing Flux Core Mig Wire for Positional Welding
Upgrade your hardfacing operations with the Welding Alloys LP-G Flux Core Mig Wire¡ªengineered for all-positional welding in high-wear applications. This 1.2mm diameter wire delivers exceptional abrasion resistance and impact strength, making it ideal for critical components in agricultural, earthmoving, and recycling machinery. Achieve precise, vertical welds with minimal effort and maximize productivity on-site.
Core Specifications
| Wire Diameter | 1.2mm |
| Spool Weight | 15kg |
| Hardness (3 layers) | 55-60 HRC |
| Shielding Gas | Argon 5/2 or similar mixed gas |
| Polarity | DC+ |
| Optimum Current | 220 Amps |
| Optimum Voltage | 22 Volts |
| Stick-out Range | 15-25mm (Optimum: 20mm) |
| Classification | AS/NZS 2576-2005 1855-B5, EN 14700 TFe8 |
| Deposit Type | Martensitic Steel (Medium Alloy) |
Key Benefits
- All-Positional Versatility: Flux core design enables vertical welding for hard-to-reach areas.
- Superior Wear Resistance: 55-60 HRC hardness withstands metal-metal abrasion in dry/wet environments.
- Cost-Effective: Economical wire with long-lasting performance reduces downtime and replacement costs.
- Machinable Deposit: Compatible with special tools for post-weld finishing.
- High Impact Strength: Martensitic steel composition ensures durability under heavy loads.
Applications
Perfect for hardfacing components in:
- Agricultural & earthmoving equipment (bucket teeth, cutting edges)
- Compactor wheels, shredders, and recycling machinery
- Steel mill rolls, cable drums, and sand dredge equipment
- Conveyor chutes, grizzly bars, and dragline buckets
- On-site wear liner protection for corner joints and weld seams
Performance Highlights
Engineered for demanding conditions, this wire delivers consistent results with minimal spatter. The flux core stabilizes the arc, ensuring smooth bead formation even in vertical positions. Its medium-alloy composition balances hardness and toughness, making it suitable for both impact and abrasion resistance.
Quality Assurance
Complies with international standards (AS/NZS 2576-2005, DIN 8555, EN 14700) and equivalent to Stoody 965-G. Each spool undergoes rigorous testing to ensure weld integrity and performance consistency.
FAQ
Q: Can this wire be used for overhead welding?
A: Yes, it is designed for all-positional welding, including overhead applications.
Q: What tools are needed for machining the weld deposit?
A: Use carbide-tipped tools for optimal results.
Q: Is preheating required?
A: Preheating is recommended for thick sections; consult technical data for specific guidelines.
Request a Quote
Ready to enhance your hardfacing operations? Contact us today for bulk pricing, technical support, or samples. Our team of welding experts is here to help you find the perfect solution for your application.